Properties:
Good weather resistance, high chemical stability, saltwater resistance and good ultraviolet resistance. Excellent adhesion to steel and concrete.CR-5 is a newly developed product with low viscosity, it can help customers rising solid content and reaching the Chinese VOC emission standard under 420g/L in the coating formulations

Solubility:
Soluble in organic solvents (like toluene and xylene) and forming a colorless or yellow transparent solution. Insoluble in ethanol fat hydrocarbons solvents.

Stability:
Stable in an atmosphere at room temperature and slowly degrading under continuous heating. Addition of less than 1% epoxy resin with low molecular weight is suggested during the production process.

Compatibility:
Compatible with the majority of plasticizers. The most used plasticizer is chlorinated paraffin with a chlorine content of 40-52%. With chlorinated paraffin 52° for example, according to the requirements of the coating, a mixing ratio of resin to plasticizer between 2:1 and 3.5:1 is recommended. YURON CR has also a good compatibility with acrylic resin and alkyd.

Applications:
YURON CR has a good resistance to chemicals and atmosphere and good compatibility with many resins and plasticizers. It finds applications in many industrial fields, such as:
Anti-corrosive paint / marine paint / flame-retardant paint / road marking paint / adhesive
YURON CR is available in various viscosity grades. All grades are free from carbon tetrachloride (CTC).

Packaging and Storage:
20 kg/bag. Store at room temperature, free from humidity. Non-dangerous good with stable chemical properties.

Specifications:

	CR-5	CR-10	CR-20
Content of chloride (%) ≥	65
Viscosity (mPa.s)(20wt% xylene solvent 25°C)	5-8	8-13	20-30
Maximum solubility (w/w) %	60
Weight loss after drying (%) ≤	0.6
Appearance	White powder

Note: The viscosity is  measured by rotary viscometer in xylene 20% solution at 25°C 20g YURON CR dissolved in 80g xylene.